品 名

Grade

WS-CC

WS-Tetoron

WS-3753

适用标准

JIS

_

NEMA

_

CEM-3

材质

Base and resin

环氧树脂

Epoxy resin

环氧树脂

Epoxy resin

环氧树脂

Epoxy resin

试验项目

Testing item

单位

Unit

处理条件

Processing

Condition

碳纤维布

Carbon cloth

聚脂布

Tetoron cloth

玻璃纤维布

Glass fiber cloth

平行层向击穿电压

Flatwise –with stand voltage

kv/mm

C-90/20/65

-

10

-

垂直层向击穿电压

Edgewise-withstand voltage

kv

O-0.5/90

-

5

-

绝缘电阻

Insulation

resistance

常态

Normal condition

MΩ

C-

90/20/65

-

10⁶-10⁸

-

煮沸后

After boiling

MΩ

C-90/20/65

+D-2/100

-

10³-10⁵

-

体积电阻系数

Volume resistivity

MΩ-cm

C-

90/20/65

-

10⁷-10⁹

10⁸

表面电阻系数

Surface resistivity

MΩ

C-

90/20/65

-

10⁶-10⁸

-

介电常数(1MHz)

Dielectric constant

―

C-

90/20/65

-

4．0-4．5

-

介电损耗 (1MHz)

Dielectric loss tangent

―

C-

90/20/65

-

0．030-0．040

-

耐电弧性

Arc resistance

sec

A

-

-

-

耐电磨性

Tracking resistance

V(CTI)

A

-

-

-

弯曲强度

Flexural strength

垂直层向

Perpendicular to laminae

MPa

A

720-820

100-150

500

压缩强度

Compressive

strength

垂直层向

Perpendicular to laminae

MPa

A

550-600

200-290

-

平行层向

Parallel to laminae

MPa

A

360-420

100-150

-

抗张强度

Tensile strength

MPa

A

550-600

100-130

-

杨氏模量

Young’s modulus

MPa

A

88000-94000

490-780

-

粘结强度

Bonding strength

kN

A

9．5-11．0

7．0-9．0

-

洛氏硬度测量

Rockwell hardness

HR-R

A

120-125

118-122

-

埃左氏冲击强度

Izod impact strength

平行层向

Parallel to laminae

J/cm

A

3．0-3．5

0．8-1．2

-

加热后外观

Appearance after heating

℃/2hr

A

180

140

150

吸水率 (厚 1.0mm)

Water absorption(Thickness 1.0mm)

％

E -24/50

+D-24/23

0．05-0．15

0．15-0．35

0．1

比重

Specific gravity

―

A

1．55-1．65

1．3-1．4

1．9

热膨胀系数

Thermal

expansion

垂直层向

Perpendicular to laminae

1/℃

RT~ 200℃

-

4．2×10-⁴

平行层向

Parallel to laminae

1/℃

RT~ 200℃

-

耐燃性

Burning

resistance

UL-94法

―

C-48/23/50

&E-168/70

UL94V0

铁路车辆燃烧试验

Burning quality test for rolling stock

―

A